- Used with the CRL9257 Scratch Polisher
- Premium Cerium Oxide for Fast Stock Removal
- Exceptional Suspension Qualities
- Ideal for Recirculating Slurry Systems
- Contains No Zinc
- Hand or Machine Polishing
Cerium Oxide Polishing Compound
CRL Cerium Oxide is a high grade optical polishing compound used to lessen and polish scratches from mirror bevels, table top edges, glass in vehicles or structures. CRL Cerium Oxide is mixed with water to form a paste or slurry. This compound has excellent suspension qualities and will not harden. Contains no zinc oxide, and meets most local disposal ordinances. This Cerium Oxide Compound can be used with a hand pad for light surface cleanup, powered hand devices for scratch and surface repair, mechanized scrubbers in mirror silvering lines, or as the final polishing step in multi-stage edging and beveling equipment.
CRL Cerium Oxide Compounds maintain and deliver a uniform particle size, on average 2.9 micron, and a high concentration of rare earth oxides to provide the brightest possible finish in all applications. These compounds exhibit exceptional suspension quality, required for use in today's recirculating slurry systems. The added benefit of soft settling means glass and equipment are more easily cleaned and maintained.
The efficiency of the Cerium Oxide polishing process depends on two important variables: Concentration and temperature. Too much Cerium Oxide is a waste of resources while too little impairs the quality of the end product.
Cerium Oxide compounds polish glass by a combination of mechanical and chemical action. The material must reach and maintain a certain temperature to stimulate the chemical reaction. The mechanical action employs felt pads or wheels. For surface restoration, the Cerium Oxide is mixed with water to form a thin paste that is applied directly to the glass surface. A damp felt pad or wheel is then used to agitate the paste. The friction of the wheel creates the heat needed to activate the polishing process. Too much heat will dry the paste, so care must be taken to keep the paste wet at all times.
For recirculating slurry systems, the concentration of Cerium Oxide in the water is based on the specific gravity of the slurry as measured in Degrees Baume, which is measured using a Hydrometer. Measure out the proper proportions of heated water (at least 80ºF/30ºC) and Cerium Oxide into a container and mix thoroughly. Place the Hydrometer into the mixture and take a reading at the surface line. For light surface cleaning such as pre-silvering, 1º Baume (1.6 oz. of Cerium per gallon of water or 11.8 grams per liter) is sufficient. For beveling and edging, a 3º to 5º Baume (4 to 7.2 oz. per gallon, or 29.7 to 53.7 grams per liter) is recommended. Slurry temperature should be maintained between 90ºF and 105ºF (32ºC and 40ºC) for optimum performance.