Loctite 2264448 HY 4070 Hybrid Gel Adhesives, 10 mL Cartridge, Clear, 10/Case - pack of 10
Item #: 2264448 by Loctite
See reviewsSee reviews
30 Days Easy Return. We are the largest supplier of the most adaptable, personalized hardware in the industry. We work hard to ensure you're satisfied with our products.
Features
Type
Hybrid Gel Adhesive
Ratio
10:1
Applications
Bonding
VOC
< 3 %
Fixture Time
4 min to 6 min (2 mm Gap); <60 s (0.05 mm Gap)
Maximum Viscosity
1300 mPa (Part A); 30 mPa (Part B)
Language
English
Resistance
Moisture; Temperature
Application Temperature Max
+25 °C
Capacity Vol. [Nom]
10 mL
Working Time [Min]
1 min
Flash Point [Nom]
+176 °F to +199.4 °F (Part A); +230 °F (Part B)
Specific Gravity [Nom]
1.05 to 1.1
Tensile Strength [Nom]
2117 psi
Working Time [Nom]
1 min to 4 min
Adhesive Tensile Shear
0.1 N/mm²
Fix Cure Time @ Temp.
4 min to 6 min (2 mm Gap) @ +25 °C; <60 s (0.05
Elongation [Nom]
4.9 %
Gap Fill [Nom]
0.05 mm
Viscosity [Min]
1 mPa (Part B); 200 mPa (Part A)
Hardness [Nom]
65 Shore D
Viscosity [Nom]
1 to 30 mPa (Part B); 200 mPa to 1300 mPa (Part A)
Working Time [Max]
4 min
Container Size
11 g
Color
Off-White
Mixing Ratio
10
Full Cure Time
168 hr
Minimum Temperature
-40.00C
Working Time
5 min
Minimum Application Temperature (F)
302.00
Adhesive Type
Two-Part
Container Type
Dual Cartridge
Container Size Range
Smaller than 1 oz
Product Service Code
8040
Vendor Drop Ship
N
Minimum Application Temperature (C)
-40.00
Product Overview
Loctite® HY 4070 is a two-part, transparent, cloudy colorless to pale yellow cyanoacrylate/acrylic hybrid gel adhesive that provides a fast fixture at room temperature
It suits various substrates including most plastics, rubbers and metals
It is used where complete cure of excess adhesive, as well as temperature and moisture resistance, is required
Non-sag
Gel consistency prevents adhesive flow, even on vertical surfaces
Curing is initiated on mixing the Part A and Part B components
Handling strength is achieved rapidly; full strength is achieved over time.
It suits various substrates including most plastics, rubbers and metals
It is used where complete cure of excess adhesive, as well as temperature and moisture resistance, is required
Non-sag
Gel consistency prevents adhesive flow, even on vertical surfaces
Curing is initiated on mixing the Part A and Part B components
Handling strength is achieved rapidly; full strength is achieved over time.